Alumina Ceramic Porous Zirconia Tube Honeycomb Metal Refractory Casting Filter Filtro Ferro

• Type: Clay Dry Sand
• Casting Method: Liquid Metal Filtration
• Sand Core Type: Resin Sand Core
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: NINGXIN-CFF-S231104
• Application: Auto Parts
• Machining: Liquid Aluminium Filtration
• Material: Sic
• Surface Treatment: Coating
• Surface Roughness: Good
• Standard: GB
• Certification: ISO 9001:2000, ISO 9001:2008
• Size: 35mm to 200mm
• Main Material: Silicon Carbide
• Color: Grey
• Hole Density: 10/15/20/25/30ppi (Ppi=Pores Per Inch)
• Porosity: 80-90%
• Transport Package: Carton & Pallet
• Specification: As per request
• Trademark: NINGXIN
• Origin: Hebei, China
• HS Code: 690390
• Production Capacity: 5000000PCS/Month
• Package Size: 110.00cm * 110.00cm * 200.00cm
• Package Gross Weight: 500.000kg

Product Description

Product Description

Silicon Carbide SIC Ceramic Foam Filter for Foundry Molten Metal Gray Iron Ductile Iron Castings Filtration

Model Name: NINGXIN-CFF-S
Application: For the filtration of molten Iron,copper,brass,aluminum and alloy

Ceramic foam filters offer a simple, reliable and costeffective method to remove inclusions. Filtering with CFF is a supplement to metal treatment within the furnace, such as fluxing and degassing or inline filtration.

Ceramic foam filters have an open pore reticulated structure with very high porosity and surface area to trap inclusions. The open foam structures are compose of ceramic material, such as alumina, mullite or silica. Alumina is the most common filter material. Ceramic foam filters operate in a deep bed filtration mode where inclusions smaller than the pore openings are retained throughout the cross-section of the filter.

CFFs typically are a polyurethane foam coated with a ceramic slurry then dried and fired. During firing, the polyurethane foam dissipates leaving behind a porous ceramic structure. The ceramic can be a phosphate-bonded alumina and pore sizes and thicknesses can vary.
 

Main material	Silicon carbide (SIC)
Working Temperature	≤1500ºC
Color	Grey
Hole density	10/15/20/25/30PPI (PPI=pores per inch)
Porosity(%)	80‐90
Compressive Strength(MPa)	≥1.0 (Room temperature)
Bulk Density(g/cm3)	0.35‐0.55
Thermal shock resistance	≥2times/1100ºC‐Room temperature