Zirconia Investment Casting Filter 100X100X25mm 20ppi 100*100*25mm 10ppi Molten Metal Filtration

• Application: Refractory, Industrial Ceramic, Foundry Molten Metal Filtration
• Type: Ceramic Plates
• Main Material: Zro2
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: NINGXIN-CFF-Z319
• Color: Yellow
• Working Temperature: up to 1700 Degree C
• Hole Density: 10/20ppi (Ppi=Pores Per Inch)
• Porosity(%): 80-87
• Compressive Strength(MPa): 1.5 (Room Temperature)
• Bulk Density(g/cm3): 0.9-1.3
• Thermal Shock Resistance: 3times/1350 Degree C to Room Temperature
• Size: 35-200mm
• Material: Zirconia Ceramic
• Transport Package: Carton and Pallet
• Specification: As per request
• Trademark: NINGXIN
• Origin: Hebei, China
• HS Code: 690390
• Production Capacity: 200000PCS/Month
• Package Size: 110.00cm * 110.00cm * 200.00cm
• Package Gross Weight: 800.000kg

Product Description

 

Zirconia Ceramic Foam Filter for Steel Castings Filtration

Ceramic foam filters can effectively remove non-metallic inclusions including slag and dross from the molten metal stream. Additionally, foam filters aid in reducing turbulence in the gating system. Ceramic foam filter's outstanding thermal shock resistance and high strength properties were developed for superior performance in extreme metal casting foundry applications. 

Simplified pouring system and increasing pouring efficiency
The lengthy runner can be shortened when filters are used. It could greatly save scrap    recycling cost, save pouring times and improve pouring efficiency.

Remove tiny slag effectively and purify molten metal
Ceramic foam filters can adsorb nearly 0.1mm diameter tiny slags based on it's special working principle.

Well-distributed molten metal and improve performance
After purification, the casting's density and strength are improved and elongation and impact toughness is improved greatly, some extension rate even can be increased by 19-30%. Therefore, the casting mechanical properties and processing performance are improved obviously.

Reduce turbulence
The molten metal can be changed from turbulent flow to laminar flow when through the 3D structure ceramic foam filters. This could greatly reduce the casting bubble defect.
Zirconia ceramic foam filters are determined for filtering of steel and steel alloys up to the temperature of 1700 °C.
Filters are recommended especially for high quality grades of alloys.

Model Name: NINGXIN-CFF-Z
Application: For the filtration of large scale iron and steel alloy
 

Main Material	ZrO2
Working Temperature	≤1700ºC
Color	Yellow
Hole density	10/20PPI(PPI=pores per inch)
Porosity(%)	80‐87
Compressive Strength(MPa)	≥1.5 (Room temperature)
Bulk Density(g/cm3)	0.9‐1.3
Thermal shock resistance	≥3times/1350ºC‐Room temperature

 